Abstract
Industrial experiments showed, when parts are submitted to cyclic loading, fatigue life in service is not necessarily deter-mined by large cracks period. Indeed, a major part of this fatigue life is constituted by small cracks propagation. This studyaims to characterise the short fatigue crack (SC) behaviour and evaluate differences with long fatigue crack (LC) in navalsteel (S355NL).