Abstract
The tetragonal Cu2Sb-type Mn1.8Cu0.2Sb alloy was prepared by solidification under zero field and high magnetic field of 12T. No thermal hysteresis was observed. High-magnetic-field (HMF) solidification led into c-axis texture in Mn1.8Cu0.2Sb alloy. Moreover, the severity of metamagnetic transformation in a Mn1.8Cu0.2Sb alloy was steepened and the resultant magnetic entropy change was enhanced. The exchange bias at low temperature was observed. Our work demonstrated the pronounced influences of HMF solidification on the crystallographic orientation, metamagnetic phase transformation and the magnetic exchange couplings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.