Abstract
Abstract This study was carried out to explain reasons of the enhanced hydrogen entry into iron at low polarisations. Hydrogen permeation rate (HPR) through a 35-μm thick iron membrane was studied with the electrochemical technique in 0.1 M NaOH at 25 °C. A rotating split-ring disk electrode was used to detect soluble Fe(II) species. Enhanced hydrogen entry (HPR peaks) was observed at low cathodic and low anodic polarisations during voltammetric cycling, and also during galvanostatic anodic polarisation applied after cathodic charging. HPR peaks occurred at potentials from about −1.2 to −0.9 V (NHE) which were more cathodic than the potentials of thermodynamic stability of Fe(OH) 2 or Fe 3 O 4 , and of the formation of soluble Fe(II) species. It has been suggested that the enhanced hydrogen entry is associated with the presence of FeOH ad . In this species oxygen is bound with hydrogen (oxo-hydride), hence it can be supposed that the mechanism of its promoting effect can be similar to that of hydrides of other elements of the VIb group.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.