Abstract
Carbon nanotube supported nano-size monometallic and noble metal (Pt and Ru) promoted cobalt catalysts were prepared by incipient wetness impregnation (IWI) using solution of cobalt nitrate and characterized by nitrogen adsorption isotherm, X-ray diffraction (XRD), temperature programmed reduction, in situ magnetic method and TEM. Analysis of the magnetization and H2-TPR data suggested promotion with platinum and ruthenium significantly decreased the cobalt species reduction temperature. TEM and XRD results showed that the presence of noble metal promoters had no significant effect on the size of cobalt for carbon naotube as catalytic support. Promotion of cobalt carbon nanotube-supported catalysts with small amounts of Pt and Ru resulted in slight increase in Fischer–Tropsch cobalt time yield. The Pt and Ru promoted cobalt catalyst exhibited carbon monoxide conversion of 37.1 and 31.4, respectively. C5+ hydrocarbon selectivity was attained at 80.0%. The Pt promoted cobalt supported on carbon nanotube yielded better catalytic stability than that of the monometallic cobalt catalyst. Over carbon nanotube supported cobalt catalyst, the addition of noble promoter significantly decreased the cobalt reduction temperature, but had no significant influence on the cobalt particle size.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.