Progress towards a low-cost commercial coated conductor

Abstract

ABSTRACTYBCO films prepared from metal trifluoroacetate (TFA) precursors on oxide-buffered textured non-magnetic substrates have achieved performance levels equaling that on oxide buffered textured Ni substrates. Critical current densities of 0.7 MA/cm2 to 1.0 MA/cm2 have been achieved in 0.4 µm thick YBCO films on short-length of CeO2/YSZ/Y2O3/Ni/Ni-13wt%Cr substrates. High-quality epitaxial buffers comprising a Ni layer, Y2O3 seed, YSZ barrier and CeO2 cap layers have been deposited over meter long tapes of deformation textured Ni and Ni-13%Cr using reel-to-reel processes. High-performance TFA-based YBCO films have been deposited on 0.1 m to 0.3 m lengths of these oxide buffered substrates using reel to reel processes. Critical current densities up to 1.0 MA/cm2 have been achieved in 0.4 µm thick YBCO films on CeO2/YSZ/Y2O3/Ni substrates. Using multiple coats of the metal trifluoroacetate precursors, thicker YBCO films have been demonstrated on oxide buffered substrates. Critical currents in excess of 100A/cm-width have been achieved for 1.2 µm -1.6 µm thick YBCO films on short lengths of CeO2/YSZ/Y2O3/Ni substrates.