Abstract
AbstractHollow spheres of nickel oxide (NiO) and silver, gold, and platinum nanoparticle loaded NiO composites were successfully produced by using polystyrene (PS) latexes as hard template. Due to the presence of tertiary amine based diblock copolymer stabilizer on the surface of PS, the tertiary amine functional groups provided homogene deposition of nickel hydroxide, and then the precursor NiO salt production on the surface of PS latexes with a controlled precipitation technique. Then, NiO and NiO/metal NP hollow spheres were produced by calcination at 600 °C. Thermogravimetric analysis indicated that the amounts of NiO and NiO‐composite after calcination were in the range of 21.1–29.7 wt%. The diameters of metal oxide spheres were in the range of 2.0–2.7 μm and the shell thickness were in the range of 250–350 nm. These structures had very low densities due to their porous and hollow structures and had outer layers with highly rough surfaces due to formation of nanosheets, which may offer important advantages for catalysis studies.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.