Abstract
AbstractOne of the great challenges in the use of nanomaterials is their production at low costs and high yields. In this work aluminum nanoparticles, from aluminum powder, were produced by wet mechanical milling through a combination of different attrition milling conditions such as ball-powder ratio (BPR) and the amount of solvent used. It was observed that at 600 rpm with a BPR of 500/30 g for 12 h, it was possible to produce nanoparticles with a size close to 20 nm, while at 750 rpm with a BPR of 380/12.6 g for 12 h, nanoparticles of approximately 10 nm were obtained. Scanning and transmission electron microscopy confirmed that the milling product is an agglomeration of nanoparticles with different sizes. These results show the feasibility of obtaining aluminum nanoparticles by mechanical milling using only ethanol as solvent, avoiding hazardous by-products obtained from chemical routes, and the use of complicated methods such as laser ablation and arc discharge.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.