Abstract
Mechanically milled FeCrNbB feedstock powders from commercial precursors were used to produce amorphous coatings through two different industrial thermal-spraying techniques: high-velocity oxygen fuel (HVOF) and flame spraying. Microstructure, thermal behavior, and hardness of the coatings and their corrosion resistances in acidic and alkaline chloride-rich media were comparatively studied. HVOF process was effective to produce ~ 200-µm-thick highly amorphous coatings with hardness over than 700 HV0.3 and low porosity (~ 5 pct). Flame-sprayed ~ 220-µm-thick coatings were nanocrystalline, composed of α-Fe, Fe2B, FeNbB, and Fe2O3 phases and presented hardness of 564 HV0.3 and ~ 10 pct porosity. Electrochemical measurements indicated that HVOF coatings exhibit higher corrosion resistance than flame-sprayed ones thanks to the higher amorphous content and lower porosity resulting from the former processing route. Electrochemical impedance spectroscopy results demonstrated that amorphous HVOF Fe60Cr8Nb8B24 (at. pct) coatings are interesting to protect mild steels such as the API 5L X80 against corrosion in chloride-rich environments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.