Production and characterization of organic solar cells

Abstract

PurposeThe study aims to carry out the production of a bulk heterojunction organic solar cell in a laboratory scale using a blend of poly (3-hexylthiopene) (P3HT) and [6, 6]-phenyl (C61) butyric acid methyl ether (PCBM).Design/methodology/approachFour inverted geometry organic solar cells were prepared based on 1:1 ratio of P3HT to PCBM and subjected to post annealing at different temperatures of 32, 120, 130 and 140°C. Solar cells were fabricated with structure glass/ITO/P3HT:PCBM/PEDOT:PSS/Au and characterized using Keithley 2400 series sourcemeter and a multimeter interfaced to a computer system with a LabVIEW software, which showed both dark and illumination current–voltage characteristic curves. Four reference cells were also fabricated with structure soda lime glass/P3HT:PCBM and annealed at different temperatures of 32, 120, 130 and 140°C.FindingsThe third organic solar cell prepared, Sample CITO, had the best performance with power conversion efficiency (PCE) of 2.0281 per cent, fill factor (FF) of 0.392, short circuit current of −0.0133 A and open circuit voltage of 0.389 V. Annealing of active layer was found to improve cell morphology, FF and PCE. Annealing of the active layer at 140°C resulted in a decrease of the PCE to 2.01 per cent.Research limitations/implicationsThese findings are in good agreement with previous investigation in literature which reported that best annealing temperature for a 1:1 ratio blend of active material is 130°C. Ultraviolet–visible spectra on reference cells showed that sample CITO had wider absorption spectra with peak absorbance at a wavelength of 508 nm.Originality/valueThis research is purely original.