Abstract
Melt-spun Poly (Ether Ether Ketone) (PEEK) fibers were produced on a custom built melt-spinning system. Fibers of two different grades were spun at two different draw-down ratios, with one of three possible post-spinning treatments: as-spun, annealed, or hot drawn. Fibers were characterized with SEM, DSC, WAXS, and tensile testing. Hot drawn fibers had the highest degree of crystalline orientation (S = 0.81). Modulus, strength, and yield stress, were found to be 1.7 GPa, 175 MPa, and 45 MPa, respectively for as-spun fibers. As-spun fibers had strains-to-failure as high as 215%, which decreased to about 25% after hot drawing. Annealed and drawn fibers had similar crystallinity and crystalline orientation, but drawn fibers had significantly higher moduli of 2.8 GPa and 5.2 GPa, and strength of 195 MPa and 480 MPa, respectively. Fiber properties were found to be tunable to a number of combinations, with potential for numerous applications as novel biomaterials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.