Abstract
Alumina nanoparticles were synthesized from locally available high alumina clay, obtained from Giro in Kabbi State, through acid leaching with sol-gel method. The clay was leached with hydrofluoric acid and the aluminous solution produced was used as precursor to synthesis nanoparticles through sol gel process. The composition and structure of the clay and the particles produced were characterized using Fourier Transform Infrared (FTIR), X-ray diffraction and fluorescence Spectroscopic techniques, Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). From the analyses, the clay sample was observed to be high in alumina and predominantly Kaolinitic in nature. During the sol-gel process, effective flocculation was obtained at slightly alkaline pH range (7.6 to 8.0) and a relative moderate temperature of 80oC. The result also shows that the aging time of the gel affected the size of the particles produced during the process, and the particles are mainly nano-alumina.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: FUTA JOURNAL OF ENGINEERING AND ENGINEERING TECHNOLOGY
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.