Abstract
Well-sintered SDC-NC (Sm0.2Ce0.8O1.9-Na2CO3) nanocomposites have been prepared through a rare-earth/sodium complex carbonate precipitation, powder prefirings at the temperatures 400, 500 and 600 °C and sintering at 800 °C. Their sintering performances, phase components and microstructures have been characterized by Archimedean method, XRD and FESEM techniques. In particular, the influence of the interfacial interactions between the phases of SDC and NC on the microstructures and electrical conductivities of SDC-NC nanocomposites have been investigated by AC impedance and Raman spectroscopies. It has been found that on the basis of the fitting analysis of AC impedance data, the oxide ionic and protonic conductivities of interfacial and non-interfacial phases in the SDC-NC nanocomposites are found to be strongly dependent upon their prefiring temperatures with the sample of SN-600 showing the highest values of 73.2/33.7 and 51.1/105.4 μS/cm at 300 °C, respectively. The single cell based on the electrolyte of SN-600 presents an OCV of 0.992 V and peak power density of 421 mW/cm2 at 550 °C. The interfacial interactions between the phases of SDC and NC inside SDC-NC nanocomposites are considered responsible for their differences in microstructure and electrical conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.