Abstract
The long tape process was developed using the advanced TFA precursor solution. In a long tape production, the advanced TFA precursor solution was coated by a die-coater using the reel-to-reel system, and the multi-coating method was applied for thicker film fabrication. We successfully fabricated long uniform precursor films. In the high temperature treatment, a large scale equipment for the continuous long tape process was developed. This equipment had a perpendicular gas flow system to the tape length which is effective to fabricate the uniform films. I c values and its distribution in the YBCO tape fabricated by this method on CeO 2/IBAD-Gd 2Zr 2O 7/Hastelloy were measured. And the uniform and high performance was confirmed. A 0.25 m long YBCO film with 1.38 μm in thickness on the metal substrate shows the high I c performance of 210 A with end to end at 77.3 K in self-fields.