Abstract
ABSTRACTTlBA2Cu3Ox and Tl2Ca2Cu3Ox powders were synthesized, loaded into Ag tubes, and worked into wires and tapes by drawing and rolling. All processing outside of furnaces was in a dry-N2 glovebox. All heat treatments were performed in O2. The Ag-clad wires fabricated from these powders exhibited onset of superconductivity at ≈118 K and critical current densities at 77 K of 2 × 103 to 4 ×103 A/cm2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.