Processing and properties of PLA/Mg filaments for 3D printing of scaffolds for biomedical applications

Abstract

PurposeThis paper aims to develop a novel strategy to manufacture poly-lactic acid (PLA) filaments reinforced with Mg particles for fused filament fabrication of porous scaffolds for biomedical applications.Design/methodology/approachThe mixture of PLA pellets and Mg particles was extruded twice, the second time using a precision extruder that produces a filament with zero porosity, constant diameter and homogeneous dispersion of Mg particles. The physico-chemical properties of the extruded filaments were carefully analysed to determine the influence of Mg particles on the depolymerisation of PLA during high temperature extrusion and the optimum melt flow index to ensure printability.FindingsIt was found that the addition of a polyethylene glycol (PEG) plasticizer was necessary to allow printing when the weight fraction of Mg was above 4%. It was possible to print porous face-centre cubic scaffolds with good geometrical accuracy and minimum porosity with composite filaments containing PEG.Originality/valueThe new strategy is easily scalable and seems to be very promising to manufacture biodegradable thermoplastic/metal composite filaments for 3D printing that can take advantage of the different properties of both components from the viewpoint of tissue engineering.