Abstract
Deformation dilatometry and semi-industrial extrusion were used to investigate the effect of different thermomechanical processing routes on the microstructure and mechanical properties of the low-alloy Mg alloys ZX10 (Mg–1Zn–0.3Ca) and ZX00 (Mg–0.5Zn–0.15Ca). It is shown that the deliberately adjusted formation of intermetallic particles beneficially influences dynamic recrystallization and grain growth, with the result of a fine-grained microstructure (grain size<2μm). The presence of unrecrystallized regions with its unfavorable influence on ductility and mechanical anisotropy can be controlled by the selection of an indirect extrusion mode. Meta-dynamic recrystallization generates almost fully recrystallized microstructures and hence the desired properties, which are characterized by high strength (yield strength≈240MPa), simultaneously high ductility (elongation to fracture≈30%), and low structural and mechanical anisotropy. These properties are of great interest for light-weight applications and for deployment as biodegradable implants in medical technology.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.