Abstract
In this study, we focus on methods to further improve the flux pinning and critical current density (Jc) of disk shaped MgB2 bulk superconductors by a comparative study with locally obtained charcoal at optimized processing conditions. The doping of charcoal was varied at 0, 0.2, 0.4 and 0.6 wt%. Bulk MgB2 samples were produced by in-situ solid state reaction in Ar gas and ambient pressures at 775 °C, employing high purity of Mg metal and nano B powder mixed in a fixed ratio of Mg:B = 1:2 and optimal conditions. The phase has been investigated by X-ray diffractometer (XRD). The effects of the dopants on superconducting properties especially the field dependence of Jc have been determined by superconducting quantum interference device (SQUID) and critical temperature (Tc). Measurements of the magnetic susceptibility showed sharp superconducting transitions (ΔTc ∼ 1 K). Jc at self-field and 20 K was determined to be ~280 and 467 kA/cm2 for the 0 and 0.4 wt% charcoal added samples respectively. The structural and superconducting results were correlated with the addition of charcoal in the final product.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.