Abstract
Researchers at the Naval Air Warfare Center Weapons Division (NAWCWD) and Wright-Patterson Air Force Base (WPAFB) investigated poly[2-methoxy-5-(2’-ethylhexyloxy)-1,4-phenylene vinylene], (MEH-PPV) for its potential corrosion-inhibition properties on aerospace aluminum alloy AA2024-T3. Solution processing of the polymer, as well as adhesion testing and accelerated weathering tests were performed on MEH-PPV full military aerospace coatings. Wet and dry tape adhesion testing, as well as pencil hardness, impact flexibility and pneumatic adhesion tensile test instrument (PATTI) testing were used to demonstrate the adhesion performance of MEH-PPV on aluminum substrates. The results showed that MEH-PPV had acceptable adhesion characteristics when compared to hexavalent chromium (Cr(VI)) based coatings in all of these tests. Accelerated weathering analysis was performed on MEH-PPV coatings to determine their corrosion protection and weathering resistance capabilities. These tests included neutral salt spray (NSS) exposure and xenon-arc lamp testing. The results showed that while MEH-PPV does not exhibit significant color change after 500 hours of xenon arc lamp exposure, the polymer has poor corrosion protection performance under aggressive salt environments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.