Abstract
AbstractTernary composites based on glass fiber reinforced polyethersulfone (gPES) modified by a liquid crystalline copolyester (R5) were obtained by injection molding at different nozzle temperatures and at LCP contents up to 20%. The blends showed two pure amorphous phases. The ability of R5 to improve processing was seen mainly in the increase in the MFI of the blends on 5% LCP addition, which was more than 75% and 16% with respect to that of pure gPES and PES, respectively. The best processing temperature appeared to be 330°C, as it led to the maximum skin fibrillation and provided both the best small strain and fracture mechanical properties. The blend processed at 330°C with 5% R5 showed the best balance of properties because, besides the highest relative processability increase, it led to maximum values in all mechanical properties measured. This was due to both the overall fibrillation of the skin and to its having the highest ductility.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.