Process Parameter Optimization of 2507 Super Duplex Stainless Steel Additively Manufactured by the Laser Powder Bed Fusion Technique

Abstract

Laser powder bed fusion is an attractive technology for producing high-strength stainless steel alloys. Among the stainless steels, 2507 super duplex stainless steel (2507 SDSS) is known for its excellent combination of corrosion resistance and high strength. Although there are some studies that aimed at optimizing the laser powder bed fusion (LPBF) printing parameters to print highly dense 2507 SDSS parts; However, a full optimization study is not reported yet. This study aims at optimizing the printing parameters for 2507 SDSS, namely: laser power, scan speed, and hatch distance. The response surface methodology was used in generating a detailed design of experiment to investigate the different pore formation types over a wide energy density range (22.22–428.87 J/mm3), examine the effects of each process parameter and their interactions on the resulting porosity, and identify an optimized parameter set for producing highly dense parts. Different process parameters showed different pore formation mechanisms, with lack-of-fusion, metallurgical or gas, and keyhole regimes being the most prevalent pore types identified. The lack-of-fusion pores are observed to decrease significantly with increasing the energy density at low values. However, a gradual increase in the keyhole pores was observed at higher energy densities. An optimal energy density process window from 68.24 to 126.67 J/mm3 is identified for manufacturing highly dense (≥99.6%) 2507 SDSS parts. Furthermore, an optimized printing parameter set at a laser power of 217.4 W, a scan speed of 1735.7 mm/s, and a hatch distance of 51.3 µm was identified, which was able to produce samples with 99.961% relative density. Using the optimized parameter set, the as-built 2507 SDSS sample had a ferrite phase fraction of 89.3% with a yield and ultimate tensile strength of 1115.4 ± 120.7 MPa and 1256.7 ± 181.9 MPa, respectively.