Abstract
In this study, the influence of operating parameters on the relative density and microhardness property of a septenary equiatomic Ti-Al-Cr-Nb-Ni-Cu-Co high entropy alloy developed via spark plasma sintering (SPS) process was investigated at constant heating rate (100 °C/min), dwell time (5 min), pressure (50 MPa). Using response surface methodology (RSM) on the sintering temperature (ST) and milling time (MT) as the process variable parameters, a predictive model was established. The design of experiment approach was employed to minimize numbers of runs of experiment, which invariably eliminates trial by error associated with traditional experimental methods. MT and ST were taken as the variables towards the development of the design model. The optimum operating parameters were predicted using the user-defined design (UDD) under RSM and the result was validated through experiments. Observation from the results shows that MT and ST play a significant role in achieving high densification, which translates to high hardness. At 900 °C ST and MT of 10 hours, the highest hardness value of 580.1 HV, densification of 99.98%, and percentage porosity of 0.02% were recorded.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call