Probabilistic high cycle fatigue behaviour of nodular cast iron containing casting defects

Abstract

ABSTRACTTheoretical and experimental investigations were combined to characterize the influence of surface casting defects (shrinkages) on the high cycle fatigue (HCF) reliability. On fracture surfaces of fatigue samples, the defect is located at the surface. The shape used for the calculation is a spherical void with variable radius. Finite‐element simulations were then performed to determine stress distribution around defects for different sizes and different loadings. Correlated expressions of the maximum hydrostatic stress and the amplitude of the shear stress were obtained by using the response surface technique. The loading representative point in the HCF criterion was then transformed into a scattering surface, which has been obtained by a random sampling of the defect sizes. The HCF reliability has been computed by using the Monte Carlo simulation method. Tension and torsion fatigue tests were conducted on nodular cast iron with quantification of defect size on the fracture surface. The S–N curves show a large fatigue life scattering; shrinkages are at the origin of the fatal crack leading to the final failure. The comparison of the computed HCF reliability to the experimental results shows a good agreement. The capability of the proposed model to take into account the influence of the range of the defect sizes and the type of its statistical distribution has been demonstrated. It is shown that the stress distribution at the fatigue limit is log‐normal, which can be explained by the log‐normal defect distribution in the nodular cast iron tested.