Abstract
A predicting program for pipe break probability based on thermal aging embrittlement was developed. In order for life prediction, evolutions of fracture toughness and tensile strength were estimated for a Z3CN20-09M piping steel using the Argonne National Laboratory (ANL) procedure. To understand the influence of thermal aging on failure probability, different evolutions of fracture toughness, tensile strength and fatigue crack growth rate were employed in the prediction of cumulative failure probability. The results show that the cumulative failure probability for 40-year thermal aging increases by almost four times compared to without consideration of fracture toughness degradation. The cumulative failure probability is slightly affected by fatigue crack growth rate. The increase of tensile strength due to thermal aging reduces the risk of pipe failure. This work demonstrates that the degradation of fracture toughness due to thermal aging should be fully considered in the probabilistic fracture mechanics analysis of nuclear pressure pipes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.