Abstract
Purpose of this paper is presentation of forms of hydrogen degradation in steel along with pointing out methods for hydrogen degradation prevention. The paper outlines influence of nitrided layer on 34CrAlNi7-10 steel to its susceptibility to hydrogen degradation. Investigation was carried out with the use of slow strain tensile rate test (SSRT). Fracture surfaces after SSRT test were examined with scanning electron microscope (SEM) to reveal a mode and mechanism of cracking.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.