Abstract
Pressureless sintering to obtain high density boron carbide-titanium diboride composites by in-situ reaction was studied. Pressureless sintering behavior of this material was investigated between 1800-2150 .The effects of composition, sintering temperature and tine were examined. Density up to 98.5% T.D. was reached at 2150. Maximum values of flexural strength (502 MPa), hardness (33 Gpa) and fracture toughnes (4.6 MPa·m1/2) were observed in the specimens containing 15 vol.% TiB2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.