Abstract
Silicon carbide ceramics were pressureless joined by using Ti foil and Si powder, which generated Ti3SiC2 phase as the interlayer. The phase composition, microstructure and the shear strength were investigated. It was revealed that the SiC assembly after joining at 1500oC showed the high shear strength of 76.2 ± 19.5 MPa. The secondary phase of TiC within the interlayer was expected to contribute to densification improvement of Ti3SiC2 phase and thermal stress reduction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.