Abstract
The effects of hydrostatic pressure at ambient temperature on the structural and dielectric properties of PbFe0.5Nb0.5O3 (PFN) were investigated using second harmonic generation (SHG) and powder x-ray diffraction measurements to 31 GPa. The results demonstrate that PFN undergoes a pressure-induced structural transition from the R3m ferroelectric to the R3¯m paraelectric phase. SHG measurements showed a continuous decrease in the signal with pressure and complete disappearance at 7.1 GPa. Effective nonlinear optical coefficients were determined from the SHG data, and their pressure behavior was used to infer the nature of the transition. The loss of the SHG signal is accompanied by drastic changes in line widths of Bragg reflections, but no discontinuous change in volume was observed. The pressure-volume data were fit to various equations of state, and a bulk modulus K0 = 136 (±2) GPa, bulk modulus pressure derivative K0′ = 4.0 (±0.2), and initial volume V0 = 64.5 (±0.1) Å3 were obtained.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.