Abstract
Solid solutions of (1−x)LaFeO3–(x)PbTiO3 (0<x<1) have been prepared by conventional solid-state reaction. These complex perovskites have been studied by means of X-ray (XRPD) and neutron powder (NPD) diffraction, complemented with dielectric, magnetic, heat capacity and Mössbauer measurements. Complete solubility in the perovskite series was demonstrated. The NPD and XRPD patterns were successfully refined as orthorhombic (x≤0.7) and tetragonal (x≥0.8). A composition-driven phase transformation occurs within the interval 0.7<x<0.8. The samples with x<0.5 showed evidence of long-range magnetic ordering with an G-type antiferromagnetic arrangement of the magnetic moments of the Fe3+ cations in the B-site with propagation vector k=(0,0,0). Based on the obtained experimental data, a combined structural and magnetic phase diagram has been constructed. The factors governing the structural, dielectric and magnetic properties of (1−x)LaFeO3–(x)PbTiO3 solid solutions are discussed, as well as their possible multiferroicity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.