Preparation SiC Ceramic Composite Filtration Membrane Materials by Dry Pressing and Synchronous Sintering Method

Abstract

Silicon carbide ceramic composite filter membrane materials were prepared by dry pressure molding and synchronous sintering process at sintering temperature of 1300oC for 3h. and research the influence of on the molding pressure structure of SiC filtration membrane,effect of particle size on porosity, average pore size and filter pressure drop of filtration membrane, SEM was performed to examine the morphology, The porosity ,average pore size and filter pressure drop of filtration membrane were tested by Archimedes method ,bubble point method and filter pressure drop instrument. It is demonstrated that while the molding pressure (F) varied from 1MPa to 10MPa, the filter membrane material achieved preferable morphology and best performance when F equals to 5MPa. Under this modeling pressure, while silicon carbide particle size increased from 1 to 23μm, the pore ratio decreased from 48.0% to 36.2% and the average pore size increased from 0.35μm to 9.4μm, while the air gas velocity changed from 0 to 0.112m/s, the filter pressure drop increased, when the velocity is stable, the filter pressure drop reduced as the silicon carbide particle size.