Abstract
Waterborne UV curable polyurethane emulision containing C=C bond was prepared with self-emulsification. 3% water soluble photoinitiator was added to the polyurethane emulision, and polyurethane films was prepared by ultraviolet irradiation. The structure of the polyurethane emulision and films were confirmed by means of Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and thermogravimetric analysis. FTIR test result shows that cross linking and solidification reaction of C=C double bond happened after UV irradiation. When C=C content increases, the particle size of polyurethane emulision increases, crosslinking degree of films increases, water resistance and heat resistance have both been improved. When C=C content is 8.51%, gel content is more than 90% and the lowest water absorption can be 12.5%.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.