Abstract
In this paper, non-agglomerated monodispersed ultra-fine copper metallic powders have been synthesized with chemical reduction method. Fine lead-free glass powders were also prepared by solid synthesis process. Thick film paste prepared by above-mentioned copper metallic powders and lead-free glass powders was applied as conductive paste of MLCC. Mixture of glass and zinc oxide give the thick film a high adhesion strength which is attributed to the rough interface from interfacial reaction between glass and chip, and a good densification. Diffusion of metal between copper thick film and nickel thick film is clear. Ni–Cu solid solution appears under high temperature firing.