Abstract
The TiO2-Pt hybrid nanofibers with an average dia. 72.6 nm were fabricated by electrospinning poly(vinylpyrrolidone)-ethanol solution containing platinum acetate and titanium tetraisopropoxide, followed by calcination in air at 500 °C for 3 h. High resolution TEM showed that Pt nanoparticles with an average diameter of ∼2 nm were well dispersed in the anatase TiO2 nanofibers. Compared to pristine TiO2 nanofibers (average dia. 67.7 nm), the incorporation of Pt nanoparticles into TiO2 nanofibers can greatly enhance the oxidation of hydrazine in neutral solution. The amperometric hydrazine sensor, using the as-prepared TiO2-Pt hybrid nanofibers as the electrochemical catalyst, shows a wide linear range (up to 1.03 mM), a good limit of detection (0.142 µM), and a high sensitivity of 44.42 µA mM(-1) cm(-2). In addition, the excellent anti-interference property, free of matrix effect from real water samples and good reproducibility make the developed hydrazine sensor promising for real applications.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.