Abstract
We investigated the effect of different formulation strategies on the preparation of TiO2 screen printable pastes starting from the same organic colloidal suspension for dye-sensitized solar cells (DSSCs) application. As first strategy, we developed TiO2 pastes starting from nano-crystalline powder dried from the synthetized suspension, with and without an additional acid treatment, obtaining non-transparent scattering sintered layers. Instead, we demonstrate that starting from the sol solution is a key factor to obtain a well nano-dispersed TiO2 paste. The novel paste process resulted in a final homogeneous and semitransparent porous layer (T>80% @450–550nm). In order to evaluate the properties of TiO2 powders and inks we performed thermal analysis, BET and FTIR measurements. The films were screen printed on FTO (fluorinedoped tin oxide) glass and characterized after sintering via profilometry, FE-SEM analysis and UVVis spectra measurements. The photo-anode was further validated in small (2cm2) and large (90cm2) active area DSSCs, giving an average photovoltaic efficiency respectively of 5,22% and 2,39%, comparable with commercially available TiO2 paste with similar composition.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.