Abstract
The TiO2-activated carbon fiber (ACF) was successfully prepared by electrospinning and thermal treatment. The nanofiber was characterized by scanning electron microscopy (SEM), thermogravimetric-differential thermal analysis (TG-DTA), X-ray diffraction (XRD) and Brunner-Emmett-Teller method (BET). The results showed that the average diameter of ACF was in the range 200-500 nm, and the preoxidation temperature and carbonation temperature were 250°C and 500°C, and the anatase TiO2 appeared in fiber after carbonation, and TiO2-ACF specific surface area was 1146.7 m2/g. The TiO2-ACF was used for adsorption of low concentration SO2. The results showed that the adsorption rate increased with an increase in SO2 concentration, furthermore the adsorption rate increased with prolonged adsorption time, the high adsorption rate was 67.6% after 40 min. While temperature was below 60°C, the adsorption rate decreased as the temperature increased, however when temperature was above 60°C, there was a slight increase of adsorption rate as the temperature increased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.