Abstract
With the rapid development of industrial production and micro-packing technology, the demand of thermal conductivity performance of materials becomes increasingly growing. Traditional metal materials have been unable to meet the use of certain special occasions. The thermal conductivity of pure polymer materials is poor, however, which can generally be changed by filling thermal conductive composite materials. This method to prepare high performance composite materials attracts more and more attention in recent years. The structures and performances of micro-nano core-shell composite particles can be designed. In this work, we synthesized a few core-shell composite particles with different sizes using sol-gel method, such as SiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> /Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> , SiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> /AlN, TiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> /Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> , Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> /AlN. The composite particles were filled into epoxy resin. The thermal conductivity and mechanical properties of SiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> /Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> composite particles filled polymer composites are improved compared to SiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> &Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> -physical mixing particles filled polymer composites. The results show that particles of core-shell structure improve the thermal conductivity coefficient of the thermal interface polymer materials and reduce the interfacial heat resistance. The storage modulus in glassy state and rubbery state of SiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> / Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> composite particles filled epoxy resin increased 15.4% and 85% compared to the 40wt% physical mixing particles filled epoxy resin and pure epoxy resin respectively. Furthermore, the bending strength of SiO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> /Al <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> composite particles filled epoxy resin is 1.9% lower than that of the 40wt% physical mixing particles filled epoxy resin. The thermal conductivity coefficient of epoxy resin with content of 30wt% micro-nano particles of core-shell structure is 34.4% higher than that of pure epoxy resin, and 8.8% higher than that of 30wt% physical mixing particles filled epoxy resin composite. It indicated that the composite particles of core-shell structure have good heat conduction paths to improve the thermal conductivity of thermal interface polymer materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.