Abstract
Low-temperature hydrogen-disproportionation-desorption-recombination (HDDR) treatment of Sm-Fe alloy powder was conducted to prepare a metastable TbCu7 type Sm-Fe alloy powder with a grain size of more than a few hundreds of nanometers. While a treatment temperature above 700 °C produced the familiar Th2Zn17 type alloy, one below 600 °C resulted in successful synthesis of the TbCu7 type Sm-Fe alloy with submicron-size grains. This TbCu7 type alloy powder, however, showed no significant improvement in magnetic properties compared to the Th2Zn17 type, as its composition was estimated to be near SmFe8.5 and thus did not achieve the expected Fe-rich composition. Therefore, cross-sectional transmission electron microscope observation of the unfinished TbCu7 type alloy powder was conducted in order to explore means of forming the Fe-rich phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.