Abstract
Superconducting films of Ca-Sr-Bi-Cu oxides have been prepared by coevaporation of CaF2, SrF2, Bi, and Cu, followed by post-oxidation in wet O2. The films were characterized by four-probe resistivity measurements, Rutherford backscattering, transmission electron microscopy, x-ray diffraction, and Hall measurements. Zero resistance was achieved at ∼80 K, although evidence of traces of superconductivity at higher temperatures was seen in resistivity and Hall data. The critical current at 4.2 K was 1.0×106 A cm−2. The films were epitaxial on 〈100〉 and 〈110〉 SrTiO3 substrates. The electrical and structural properties of the films were insensitive to film composition over a wide range of stoichiometries.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.