Abstract
Although mesoporous silica particles are useful building blocks for colloidal crystals, mesoporous silica nanoparticles smaller than 100 nm with sufficient monodispersity and colloidal stability to enable thermodynamic assemblies have not been reported. Here, we report that highly monodisperse colloidal mesoporous silica nanoparticles (CMS) can be prepared by combining the preparation of colloidal mesoporous silica nanoparticles with a shortened nucleation time. The nanoparticles exhibited a uniform shape and relatively smooth surface because an undesirable aggregate dispersion process was avoided. In addition, the diameter of the nanoparticles was controlled by seed-growth without spontaneous nucleation, which enabled the investigation of fundamental CMS properties. Using monodisperse CMS, the dependence of the ζ-potential of CMS on the diameter was revealed. Colloidal crystals composed of mesoporous silica nanoparticles were fabricated by drying the colloidal solution. This is the first report regarding the fabrication of colloidal crystals composed of mesoporous silica nanoparticles with a small particle size.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.