Abstract
As a porous brittle material, oil well cement in oil and gas well cementing is difficult to bear complex loads, which can easily lead to the failure of the mechanical integrity of cement sheath. In this paper, SiO2 coating-CF toughening material was obtained by SiO2 modified carbon fibers (CFs) surface. In addition, the mechanical properties and mechanism of SiO2 coated-CF cement stone were discussed. The obtained results showed that the mechanical properties of SiO2 coated-CF cement paste are significantly improved. After 14 days of curing, the compressive strength can reach 32.98 MPa and the tensile strength is increased by 162%. The CF after adding SiO2 surface film improves the adhesion between the interface and the fiber by forming chemical bonds at the bonding surface with the cement paste, so as to improve the CF reinforced cement paste.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.