Abstract
CuMn-spinel thin films were prepared on aluminum substrates by the so-called dip-coating method. The layers were deposited from alcoholic solutions based on nitrate precursors and subsequently sintered in air at 500 °C. Reflectance spectra in the NIR–vis–UV interval were measured for samples with different composition and thickness. The absorber quality of the films was checked by calculating the solar absorptance. The films displaying the best reflectance spectra and the highest solar absorptances ( α s>0.87) were deposited from solutions containing molar ratio Cu/Mn=1. The analysis of composition showed that Cu/Mn ratio in the film was very close to the ratio in the dip-in solution and supported the formation of a spinel-like material of stoichiometry Cu 1.5Mn 1.5O 4. Solar absorptance was dramatically improved when a SiO 2 antireflective layer was deposited onto the spinel. By optimizing film thickness of both CuMn-spinel and SiO 2 layers optical parameter values as good as α s=0.94 and ε T(1 0 0)=0.06 were achieved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.