Preparation of polyurethane foams using liquefied oil palm mesocarp fibre (OPMF) and renewable monomer from waste cooking oil

Abstract

The aim of this research is the production of polyurethane (PU) foams with biopolyols from liquefied oil palm mesocarp fibre (OPMF) and renewable monomer. Liquefaction of OPMF was studied using polyhydric alcohol (PA) which is PEG-400 as liquefaction solvents in conventional glass flask. In the second part of this paper was obtained the PU foams which presented good results when compared with commercial foams and include polyols from of fossil fuels. PU foams were prepared by mixing liquefied OPMF biopolyol, renewable monomer from waste cooking, additives and methylene diphenyl diisocyanate (MDI). Water was used as an environmental friendly blowing agent. The factors that influence the cell structure of foams (i.e., catalyst, surfactant, dosage of blowing agent, and mass ratio of biopolyol to renewable monomer were studied. The synthesized PU foams were characterized by FTIR and SEM. The formulation of the PU foams should be improved, but the results show that is possible the use biopolyols and renewable monomer to produce industrial foams with lower cost.The aim of this research is the production of polyurethane (PU) foams with biopolyols from liquefied oil palm mesocarp fibre (OPMF) and renewable monomer. Liquefaction of OPMF was studied using polyhydric alcohol (PA) which is PEG-400 as liquefaction solvents in conventional glass flask. In the second part of this paper was obtained the PU foams which presented good results when compared with commercial foams and include polyols from of fossil fuels. PU foams were prepared by mixing liquefied OPMF biopolyol, renewable monomer from waste cooking, additives and methylene diphenyl diisocyanate (MDI). Water was used as an environmental friendly blowing agent. The factors that influence the cell structure of foams (i.e., catalyst, surfactant, dosage of blowing agent, and mass ratio of biopolyol to renewable monomer were studied. The synthesized PU foams were characterized by FTIR and SEM. The formulation of the PU foams should be improved, but the results show that is possible the use biopolyols and renewable ...