Abstract
Narrowly dispersed poly(BMA-co-MMA) and PBMA latices with particle diameters ranging within 216-435 nm were synthesized successfully by surfactant-free emulsion polymerization with KPS and AIBA. The average particle diameter and particle size distribution, average molecular weight and its distribution, glass transition temperature, reflectance spectra in visible wavelength, and refractive indices for the respective poly(BMA-co-MMA) latices and their photonic crystals were systematically investigated in terms of BMA/MMA ratio, BMA content, polymerization temperature, and DVB effect. The rate of polymerization increased with increasing MMA concentration in BMA/MMA ratio. The particle diameter increased with BMA concentration in BMA/MMA ratio. The molecular weight increased with BMA concentration in BMA/MMA ratio and monomer concentration. The drying of the latices offered self-assembled shiny colloidal crystal films showing the characteristic structural colors in visible wavelength. All the poly(BMA-co-MMA) latices prepared in the study were fallen within the range of photonic grade microspheres. The reflectance measurement on the colloidal photonic crystals having different particle diameters clearly exhibited narrow stopbands. The reflection maxima (λ(max)) measured in this study were well close to the λ(max) calculated, derived from the Bragg's equation. The refractive indices of poly(BMA-co-MMA) photonic crystals were found to be almost same as the theoretical values and increased proportionally from 1.50 to 1.57 with BMA content in BMA/MMA ratios. It was, thus, found that the optical reflectance properties of the poly(BMA-co-MMA) colloidal photonic crystals can be controlled easily by adjusting the reaction conditions and BMA/MMA ratio in soap-free emulsion copolymerization of BMA and MMA.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.