Abstract
Lanthanum-modified lead zirconate-titanate (PLZT5/54/46) powders were prepared from the commercial PbO, La2O3, TiO2 and ZrO2 powders by high-energy ball milling process. The synthesized powders milled for different hours were characterized using XRD and SEM. Thedesigned PLZT perovskite phase was formed from the mixture of the starting materials after milling for 20 hours. PLZT(5/54/46) ceramics were obtained using the produced powders milled for 20 h followed by sintering at temperatures ranging from 1000 to1200°C. Ferroelectric property of the PLZT ceramics was also measured.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.