Abstract
In this paper, preparation of SrAl2O4:Eu,Dy luminescent pigment has been investigated. Coprecipitation as a low cost and facile method was selected. X-ray diffraction patterns indicated the formation of SrAl2O4:Eu,Dy phase through calcinations process above 800 °C. Moreover, a few amount of silica caused the structural transformation to alumina silicate phase. Transparent glaze which consist of a few amount of luminescent pigment was obtained at 600° C under different atmosphere conditions. The photoluminescence properties of luminescence glaze revealed that the firing atmosphere has vital effect on luminescence features of coating glaze. Although, the luminescence decay of glaze was completely eliminated in oxide atmosphere, but the green afterglow of obtained sample was remained in argon atmosphere.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.