Abstract
Nitrogen-doped cellulose-based porous carbon materials were obtained by hydrothermal method and KOH chemical activation together with melamine as a nitrogen-doping precursor. The effects of hydrothermal temperature on the microstructure and surface morphology of the products were mainly studied. Also, the carbon dioxide adsorption capacity of the prepared porous carbon was investigated. It was found that when the hydrothermal carbonization temperature was 270 °C and the mass ratio of cellulose and melamine was 1:1, the largest micropore specific surface area of 1703 m2·g–1 and micropore volume of 0.65 cm3·g–1 were obtained, with a nitrogen-doping composition of 1.68 atom %. At the temperature of 25 °C and under the pressure of 0.1, 0.2, 0.3, and 0.4 MPa, the adsorption amount of CO2 was 1.56, 3.79, 5.42, and 7.34 mmol·g–1, respectively. Also, the adsorption process of CO2 was in good accordance with the Freundlich isotherm model.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.