Nanosized single crystals of hematite with a very narrow particle size distribution were prepared by mechanical activation of two different goethite samples. Both goethite samples transformed completely into hematite after 70 h grinding time. Transmission electron microscopy showed that the final particles were spherical in shape and of ∼17 nm average particle size. This particle size was coincident with that estimated from specific surface measurements, indicating that the hematite samples consisted of nonporous and nonaggregated particles. The crystallite size, calculated from the broadening of the XRD peaks, in the hematite samples indicated that particles consisted of single crystals. No influence of the precursor was observed in the products, so both goethite samples yielded identical rounded single crystals with a narrow particle size distribution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.