Abstract
Nanocrystalline structures offer opportunity for the development of soft magnetic materials, such as 80 wt% Ni–20 wt% Fe, with superior properties. In recent years, nanocrystalline 80Ni–20Fe (wt%) alloy has been prepared by mechanical alloying of elemental powders. However, retention of nanocrystallinity during consolidation of powder is the key issue to take advantage of improved magnetic properties. In the present work, it has been shown that near-full density bulk nanocrystalline 80Ni–20Fe strip can be prepared via a route consisting of mechanical alloying, cold compaction, sintering, and multi-step unsheathed hot rolling. A crack-free strip of nanocrystalline 80Ni–20Fe, having 99% theoretical density and a grain size of approximately 55 nm, was successfully prepared by sintering and hot rolling of mechanically alloyed powder preforms at 1140 °C. The bulk nanocrystalline 80Ni–20Fe material resulted in a very narrow hysteresis loop indicating a very small hysteresis loss. The present study shows that mechanical alloying–sintering–hot rolling route can be a promising method for producing bulk nanocrystalline materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.