Abstract
Mullite fibers were synthesized from an aqueous solution of aluminum isopropoxide, aluminum nitrate and tetraethylorthosilicate by the Sol-Gel method. The starting solution was prepared by adding aluminum isopropoxide and tetraethylorthosilicate simultaneously to an aluminum nitrate aqueous solution. The spinnability of the starting solution was investigated by varying the molar ratio of aluminum isopropoxide/aluminum nitrate in the solution. Gel fibers were obtained from solutions in a composition range of aluminum isopropoxide/aluminum nitrate of 3 to 5. Gels obtained from spinnable solutions appeared to have high homogeneity in the mixing of the Al/Si components, leading to a sharp 980°C exothermic peak in the DTA curve and a mullitization temperature of 1000°C. However, in the case of gels obtained from unspinnable solutions, a small 980°C exothermic peak was detected, and the mullitization temperature was as high as 1200°C, probably due to greater heterogeneity in the mixing of the Al/Si components.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.