Abstract
Four different alumina content of mullite ceramics were fabricated by powders synthesized using the sol-gel method. The synthesis process of powders, microstructure evolution, mechanical and optical properties of the mullite ceramics were studied. The XRD results showed that the precursors transformed into aluminosilicate spinel phase at 1000 °C and mullite phase at 1200 °C. Equiaxial grains were easy to form in the alumina-rich mullite ceramics while elongated grains were easy to form in the alumina-poor mullite ceramics. With the increase of alumina content, the grain size of the samples firstly increased and then decreased, the number of elongated grains decreased while equiaxed grains increased. The flexural strength, compression strength, fracture toughness, and Vickers hardness all decreased firstly and then increased. While the infrared transmittance increased firstly and then decreased. The transmittance at 4 μm (thickness of 0.75 mm) of the ceramics containing 66mol% Al2O3 reached the highest (72%) when sintered at 1780 °C because of the equiaxial grains.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.