Abstract
Novel main-chain-type and side-chain-type sulphonated poly(ether ether ketone)s (MS-SPEEKs) are synthesised by reacting the sulphonic acid groups of pristine SPEEKs with 2-aminoethanesulphonic acid to improve the nano-phase separated morphology of the material. 1H NMR and FT-IR spectroscopy are employed to determine the structure and composition of main-chain-type and side-chain-type sulphonated polymers. Flexible and tough membranes with reasonable thermal properties are obtained. The MS-SPEEKs show good hydrolytic stability, and water uptake values ranging from 15% to 30% are observed. Compared to Nafion 117 ®, the methanol permeability of the MS-SPEEKs is dramatically reduced to 8.83 × 10 −8 cm 2 s −1 to 3.31 × 10 −7 cm 2 s −1. The proton conductivity increases with increasing temperature, reaching 0.013–0.182 S cm −1. A maximum power density and open circuit voltage of 115 mW cm −2 and 0.830 V are obtained at 80 °C, respectively, which is significantly greater than the values generated with Nafion 117 ®. The introduction of pendent side-chain-type sulphonic acid groups increases the single-cell performance by more than approximately 20%; thus, the lower water diffusivity, methanol permeability, electro-osmotic drag coefficient and high cell performance indicated that MS-SPEEK is a promising candidate for DMFC applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.